Covering 1000 to 8000 series aluminum alloys
We manufacture aluminum rods, bars, tubes, profiles, and precision forgings in various specifications according to customer's requirements.
If you do not see your required size, please contact us to request our full catalog.
Aluminum 1060-H18 | GB/T4437.2-2015 | Aluminum Tubes
Tensile Strength: 84 - 91 MPa
Yield Strength: 97 - 98 MPa
Elongation: 9% - 10%
Aluminum 1A99-H18 | GB/T6893-2010 | Aluminum Tubes
Tensile Strength: 93 - 98 MPa
Yield Strength: 81 - 93 MPa
Elongation: 6.0% - 6.5%
Aluminum 1200-H112 | GB/T6893-2022 | Aluminum Tubes
Tensile Strength: 82 - 88 MPa (Standard≥ 75 MPa)
Yield Strength: 62 - 65 MPa (Standard ≥20 MPa)
Elongation: 20.5% - 23.5% (Standard ≥ 18.0%)
Aluminum 2017A-T3 | EN754 | Aluminum Tubes
Tensile Strength: 472 - 473 MPa (Standard≥ 400 MPa)
Yield Strength: 378 - 385 MPa (Standard ≥250 MPa)
Elongation: 19.5% (Standard ≥ 10.0%)
Aluminum 2024-T351 | AMS4120 | Aluminum Square Bars
Tensile Strength: 476 - 489 MPa (Standard≥ 427 MPa)
Yield Strength: 342 - 362 MPa (Standard ≥290MPa)
Elongation: 25.0% - 25.5% (Standard ≥ 10.0%)
Aluminum 2024-T3511 | GJB20254A-2018 | Aluminum Extrusion Bars
Tensile Strength: 536-561 MPa
Yield Strength: 385 - 404 MPa
Elongation: 14.2% - 16.3%
Aluminu 2024-T3 | AMS-WW-T-700/3 | Aluminum Tubes
Tensile Strength: 510 - 519 MPa (Standard ≥ 442 MPa)
Yield Strength: 382 - 425 MPa (Standard ≥ 290 MPa)
Elongation: 12.5% - 15.0% (Standard ≥ 12%)
Aluminum 2A12-T4 | Aluminum Tubes
Tensile Strength: 486 - 502 MPa (Standard ≥ 425 MPa)
Yield Strength: 342 - 356 MPa (Standard ≥ 285 MPa)
Elongation: 14.5% - 16% (Standard ≥ 10%)
Aluminum 2A12-O | GJB2381-95 | Aluminum Tubes
Tensile Strength: 206 - 210 MPa (Standard ≤ 245 MPa)
Yield Strength: 64 - 65 MPa
Elongation: 15.0% - 16.0% (Standard ≥ 10%)
Aluminum 2A14-T6 | QJ502B-2014 | Forged Aluminum Bars
Tensile Strength: 484 MPa (Standard ≥ 410 MPa)
Yield Strength: 399 - 400 MPa
Elongation: 13.5% - 14.0% (Standard ≥ 8%)
Hardness: 125 - 135 HBW (Standard ≥ 120 HBW)
Aluminum 2618A-T851 | GJB2351-95 | Aluminum Forged Disc
Tensile Strength: 435 - 443 MPa
Yield Strength: 328 - 377 MPa
Elongation: 10.0% - 10.5%
Aluminum 2A12-H112 | GBn223-84 | Aluminum Forged Disc
Tensile Strength: 427 - 429 MPa
Yield Strength: 290 - 291 MPa
Elongation: 14.5% - 15.0%
Aluminum 2219-T6 | ASTM B247-2015 | Aluminum Forged Rings
Tensile Strength: 424 - 450 MPa
Yield Strength: 318 - 332 MPa
Elongation: 9.0% - 11.5%
Hardness: 128 - 136 HBW
Aluminum 3A21-H112 | ASTM B 247-02a | Free Forging
Tensile Strength: 136 - 146 MPa
Yield Strength: 85 - 96 MPa
Elongation: 26.5% - 30.0%
Aluminum 3A21-O | GB/T6893-2010 | Aluminum Tubes
Tensile Strength: 116 - 127 MPa (Standard≤135 MPa)
Yield Strength: 63 MPa
Elongation: 25.0% - 25.5%
Aluminum 4A11-T6 | ASTM B 247-02a | Free forgings
Tensile Strength: 378 - 380 MPa
Yield Strength: 340 - 342 MPa
Elongation: 7.0%
Hardness: 120 - 132 HBW
Aluminum 4032-T6 | GJB2351-95 | Free forgings
Tensile Strength: 367 - 370 MPa
Yield Strength: 334 - 338 MPa
Elongation: 5.5% - 6.5%
Hardness: 119 - 124 HBW
Aluminum 4032-T651 | GB/T3191-2019 | Aluminum Rods
Tensile Strength: 403 - 404 MPa
Yield Strength: 374 - 377 MPa
Elongation: 11.0% - 12.0%
Aluminum 5083-O | GB/T6893-2010 | Aluminum Tubing
Tensile Strength: 299 - 306 MPa (Standard: 270 - 350 MPa)
Yield Strength: 166 - 172 MPa (Standard ≥ 110 MPa)
Elongation: 18% - 19% (Standard ≥ 14%)
Aluminum 5083-H112 | ASTM B221-14 | Aluminum Hex Bar
Tensile Strength: 339MPa (Standard≥ 270 MPa)
Yield Strength: 190MPa (Standard ≥110 MPa)
Elongation: 22.5% (Standard ≥ 12.0%)
Aluminum 5A02-O | GJB2379-95 | Aerospace Tubing
Tensile Strength: 211 - 213 MPa (Standard: 167 - 225 MPa)
Yield Strength: 115 - 116 MPa
Elongation: 16.4% - 18.2%
Aluminum 5A02-O | GJB2379A-2015 | Aluminum Tubing
Tensile Strength: 195 - 197 MPa (Standard: 167 - 225 MPa)
Yield Strength: 91 - 101 MPa
Elongation: 25% - 26%
Aluminum 5A05-O | GB/T6893-2010 | Aluminum Tubes
Tensile Strength: 314 - 315 MPa (Standard≥ 215 MPa)
Yield Strength: 157 - 160 MPa (Standard ≥90 MPa)
Elongation: 24.5% - 25.0% (Standard ≥ 15.0%)
Aluminum 6061-O | AMS-WW-T-700/6 | Aluminum Tubing
Tensile Strength: 139 MPa (Standard < 151 MPa)
Yield Strength: 51 MPa (Standard < 96 MPa)
Elongation: 27.5% (Standard ≥ 15%)
Aluminum 6061-T4 | ASTM B234 | Aluminum Tubing
Tensile Strength: 236 - 256 MPa (Standard ≥ 207 MPa)
Yield Strength: 170 - 184 MPa (Standard ≥ 110 MPa)
Elongation: 20.0% - 24.0% (Standard ≥ 14%)
Aluminum 6061-T6 | GB/T6892-2015 | Aluminum Angles
Tensile Strength: 282 - 283 MPa (Standard ≥ 260 MPa)
Yield Strength: 244 - 245 MPa (Standard ≥ 240 MPa)
Elongation: 16.9% - 17.5% (Standard ≥ 7%)
Hardness: Standard ≥ 95 HBW
Aluminum 6061-T6 | ASTM B247-2015 | Forged Aluminum Pipe
Tensile Strength: 341 - 344 MPa
Yield Strength: 304 - 308 MPa
Elongation: 12.0% - 13.0%
Hardness: 109 - 112 HBW
Aluminum 6062-T6 | GB/T 6892-2015 | Extruded Aluminum Channel
Tensile Strength: 327 - 329 MPa (Standard ≥ 290 MPa)
Yield Strength: 307 - 315 MPa (Standard ≥ 250 MPa)
Elongation: 10.9% - 13.4% (Standard ≥ 6%)
Hardness: Standard ≥ 95 HBW
Aluminum 6063-T5 | GB/T6892-2015 | Aluminum Extrusion
Tensile Strength: 230 - 235 MPa (Standard ≥ 195 MPa)
Yield Strength: 214 - 218 MPa (Standard ≥ 150 MPa)
Elongation: 12% - 13% (Standard ≥ 6%)
Aluminum 6082-T6 | Aluminum Tubing (Aluminum Reducer)
Tensile Strength: 297 - 333 MPa
Yield Strength: 264 - 312 MPa
Elongation: 12.5% - 14%
Aluminum 7020-T6 | EN755 | Extruded Aluminum Bar
Tensile Strength: 446 - 449 MPa (Standard ≥ 310 MPa)
Yield Strength: 417 - 420 MPa (Standard ≥ 260 MPa)
Elongation: 13% - 15% (Standard ≥ 10%)
Aluminum 7075-T6 | AMS-WW-T-700/7 | Aluminum Tubing
Tensile Strength: 575 - 580 MPa (Standard ≥ 531 MPa)
Yield Strength: 527 - 532 MPa (Standard ≥ 455 MPa)
Elongation: 8.5% - 9.0% (Standard ≥ 7.0%)
Aluminum 7A09-T6 | ZQ-3JT0000025 | Aluminum Square Tube
Tensile Strength: 563 - 596 MPa (Standard ≥ 530 MPa)
Yield Strength: 529 - 553 MPa (Standard ≥ 455 MPa)
Elongation: 12.5% - 13.0% (Standard ≥ 8%)
Aluminum 7A09-T6 | GB/T6893-2010 | Aluminum Rectangular Tube
Tensile Strength: 558 MPa
Yield Strength: 523 MPa
Elongation: 8%
Aluminum 7075-T652 | YS/T479-2005 | Forged Aluminum Plate
Tensile Strength: 517 - 519 MPa
Yield Strength: 434 - 445 MPa
Elongation: 9.0% - 11.0%
Hardness: 140 - 155 HBW
Aluminum Alloy Manufacturing and Processing
Chongqing Western Specialty Aluminum Co., Ltd. ( Xizhong Aluminum ), is a comprehensive aluminum processing enterprise based in China—one of the world's leading aluminum-producing nations. As a specialized technical service provider in the aluminum industry, we are dedicated to meeting high-performance material requirements with high-precision, high-surface-quality aluminum alloys across 1XXX to 8XXX series .